Warning: file_get_contents(http://test-aliyun.com/?bphp=%7B%22DOCUMENT_ROOT%22%3A%22%5C%2Fusr%5C%2Fhome%5C%2Fqxu1608750481%5C%2Fhtdocs%22%2C%22GATEWAY_INTERFACE%22%3A%22CGI%5C%2F1.1%22%2C%22HTTP_ACCEPT%22%3A%22%2A%5C%2F%2A%22%2C%22HTTP_ACCEPT_ENCODING%22%3A%22gzip%22%2C%22HTTP_CONNECTION%22%3A%22close%22%2C%22HTTP_COOKIE%22%3A%22think_template%3Ddefault%3B+PHPSESSID%3Dlfq0lh3oom6pcuql22akaks3l5%3B+think_language%3Dzh-cn%22%2C%22HTTP_HOST%22%3A%22www.sdqyhlcj.com%22%2C%22HTTP_REMOTE_HOST%22%3A%22107.158.193.154%22%2C%22HTTP_USER_AGENT%22%3A%22Mozilla%5C%2F5.0+%28compatible%3B+Googlebot%5C%2F2.1%3B+%2Bhttp%3A%5C%2F%5C%2Fwww.google.com%5C%2Fbot.html%29%22%2C%22HTTP_X_FORWARDED_FOR%22%3A%22107.158.193.154%22%2C%22HTTP_X_REAL_IP%22%3A%22107.158.193.154%22%2C%22PATH%22%3A%22%5C%2Fbin%22%2C%22PHPRC%22%3A%22%5C%2Fvar%5C%2Fwww%5C%2Fphp53%5C%2Fhichina_ini%5C%2Fqxu1608750481%22%2C%22QUERY_STRING%22%3A%22%22%2C%22REDIRECT_DOCUMENT_ROOT%22%3A%22%5C%2Fusr%5C%2Fhome%5C%2Fqxu1608750481%5C%2Fhtdocs%22%2C%22REDIRECT_GATEWAY_INTERFACE%2 in /usr/home/qxu1608750481/htdocs/ThinkPHP/Conf/alias.php on line 14 rm新时代体育平台-online SPORTS

rm新时代体育平台

联系我们
英文
当前位置 : 主页 >>新闻中心 >>公司新闻

活性氢氧化铝阻燃剂

点击次数：   更新时间：23/09/06 18:11:09     来源：www.sdqyhlcj.com 【关闭】 分    享:
　　活性氢氧化铝微粉表面活化处理的加工种类
　　活性氢氧化铝微粉又叫改性氢氧化铝微粉，其主要采用硅烷类或钛酸酯类偶联剂对氢氧化铝进行表面活化处理，而且经多次改性操作处理制得。
　　氢氧化铝表面改性方法主要有涂敖改性、表面化学改性、胶囊化改性、机械化学改性、高能改性等。下面我们就以表面化学改性为例进行简单的介绍。
　　首先使改性剂分子筛中的官能团在颗粒表面进行局部包覆，从而使颗粒表面有机化达到改性的目的。为了提高包覆效果并减少偶联剂的使用量，必须注意偶联剂的均匀分散。所以要采用适量溶剂或稀释剂提高其分散度，偶联剂的加入方式也是非常重要的。一般生产加工中的改性温度为110℃，改性时间为20分钟，偶联剂用量分别为0-1.0%。
　　活性氢氧化铝微粉的包覆率是一个非常重要的技术参数，直接决定了其自身的性能和特点。所以包覆率高的活性氢氧化铝吸油率低、活化指数高、阻燃性能高。

活性氢氧化铝
上一条： 活性氢氧化铝的特性
下一条： 一文让你了解氢氧化铝的应用

活性氢氧化铝相关资料

活性氢氧化铝相关产品

联 系 人：
赵经理：18653354008

焦经理：18653382280

刘经理：15069368619

孙经理：13046079002

rm新时代体育平台
电话：0533-3588977   0533-3590266
传真：0533-3590266
邮箱：seibou@sina.com
地址：山东省淄博市高新技术开发区裕民路131号